Heat-to-Heat Variations in Creep-Rupture Properties of Annealed 2 1/4 Cr-1 Mo Steel

[+] Author and Article Information
R. L. Klueh

Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tenn. 37830

J. Pressure Vessel Technol 105(4), 320-328 (Nov 01, 1983) (9 pages) doi:10.1115/1.3264288 History: Received February 14, 1983; Revised August 08, 1983; Online November 05, 2009

Abstract

The creep and creep-rupture properties of 13 heats of annealed 2 1/4 Cr-1 Mo steel were determined at 510 and 566°C (950 and 1050°F). The microstructures of all heats were primarily polygonal ferrite (75–80 percent); the balance was mostly bainite with 1–2 percent pearlite and scattered carbides. At each temperature the results indicated considerable data scatter for the high-stress (short rupture life) tests. As the stress was lowered, the creep and stress-rupture properties converged, which resulted in a decrease in the data scatter. Much of the variation and change in the properties could be attributed to the carbide precipitation reactions that occur in the steel.

Copyright © 1983 by ASME
Your Session has timed out. Please sign back in to continue.

References

Figures

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In