Failure Assessment on Tensile Cracked Specimens of Aluminum Alloys

[+] Author and Article Information
T. Christopher

Department of Mechanical Engineering, Government College of Engineering, Tirunelveli-627 00, India

K. Sankaranarayanasamy

Department of Mechanical Engineering, National Institute of Technology, Tiruchirappalli-620 015, India

B. Nageswara Rao

Structural Analysis and Testing Group, Vikram Sarabhai Space Centre, Trivandrum-695 022, India

J. Pressure Vessel Technol 126(3), 404-406 (Aug 18, 2004) (3 pages) doi:10.1115/1.1767862 History: Received October 04, 2003; Revised April 20, 2004; Online August 18, 2004
Copyright © 2004 by ASME
Your Session has timed out. Please sign back in to continue.


Nageswara Rao,  B., and Acharya,  A. R., 1997, “Failure Assessment on 34Cr Mo4 Grade Steel Cylindrical Pressure Vessels With an Axial Surface Crack,” Int. J. Pressure Vessels Piping, 72, pp. 157–163.
Nageswara Rao,  B., and Acharya,  A. R., 1998, “Failure Assessment on M300 Grade Maraging Steel Cylindrical Pressure Vessels With an Internal Surface Crack,” Int. J. Pressure Vessels Piping, 75, pp. 537–543.
Newman, Jr., J. C., and Raju, I. S., 1979, “Analysis of Surface Cracks in Finite Plates Under Tension or Bending Loads,” NASA-TP 1578 .
Newman, Jr., J. C., 1985, “An Evaluation of Fracture Analysis Methods,” Elastic-Plastic Fracture Mechanics Technology, ASTM-STP 896 , pp. 5–96.
Orange, T. W., Sullivan, T. L., and Calfo, F. D., 1971, “Fracture of Thin Sections Containing Through and Part Through Cracks,” Fracture Toughness Testing at Cryogenic Temperatures, ASTM-STP 496 , pp. 61–81.
Masters, J. N., Haese, W. P., and Finger, R. W., 1969, “Investigation of Deep Flaws in Thin Walled Tanks,” NASA-CR 72606 .
Bonesteel,  R. M., 1973, “Fracture of Thin Sections Containing Surface Cracks,” Eng. Fract. Mech., 5, pp. 541–554.
Hrisafovic,  N., and Ledy,  J. P., 1980, “Study on the Fracture Mechanics Phenomena in the ARIANE Program,” Acta Astronaut., 7, pp. 839–845.
Sharma,  V. M. J., Diwakar,  V., Arumugam,  S., and Lakshmanan,  T. S., 1999, “Residual Strength of Aluminium Alloy Afnor 7020,” Sci. Technol. Weld. Joining, 4, pp. 89–93.


Grahic Jump Location
Center surface crack plate under uniform tensile stress (σmax)
Grahic Jump Location
Failure assessment diagrams
Grahic Jump Location
Comparison of fracture strength estimations with test results 56789 for different aluminum alloys



Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In